AIN(氮化铝)陶瓷基片主要性能指标 |
|
|
Technical factors of
Aluminum Nitride substracts |
|
|
|
|
|
性能内容 |
性能指标 |
|
|
Property Content |
Property Index |
|
|
体积密度(g/cm3) |
≥3.30 g/cm3 |
|
|
Density(g/cm3) |
|
|
吸水率(%) |
0 |
|
|
|
Water absorption (%) |
|
|
热导率
[20℃](W/m·k) |
≥170 |
|
|
Thermal conductivity(20℃, W/m.k) |
|
|
线膨胀系数[RT-400℃](10-6/℃) |
4.4 |
|
|
Linear expansion coefficient
(RT-400℃,10-6/℃) |
|
|
抗弯强度
(MPa) |
≥330 |
|
|
Flexural strength (MPa) |
|
|
体积电阻率
(Ω·cm) |
≥1014 |
|
|
Bulk resistance (Ω.cm) |
|
|
介电常数
[1MHz] |
9 |
|
|
Dielectric constant(1MHz) |
|
|
介质损耗
[1MHz] |
3×10-4 |
|
|
Dissipation factor (1MHz) |
|
|
抗电强度
(KV/mm) |
≥15 |
|
|
Dielectric strength (KV/mm) |
|
|
表面粗糙度Ra
(μm) |
0.3~0.5 |
|
|
Surface roughness Ra(μm) |
|
|
翘曲度
(~/25.4(长度)) |
0.03~0.05 |
|
|
Camber (~/25.4(length)) |
|
|
外观Appearance |
致密、细晶Dense |
|
|
注: 1.表面光洁度经抛光处理后,Ra≦0.1μm |
|
|
2.产品各向尺寸精度通过激光划线保证,最小值±0.10mm |
|
|
3.特殊规格产品可按客户要求定制生产 |
|
|
1. Surface roughness can be reached 0.1 μm
after polished. |
|
|
2. Size tolerance can be controlled in
±0.10mm with laser machined. |
|
|
3. Special specifications can be supplied
upon requests. |
|
|
|
AIN(氮化铝)陶瓷基片产品图 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|